Analisa Pengaruh Variasi Penggabungan Asbuton dan Aspal Minyak Terhadap Campuran AC-BC
Abstract
Asbuton, which has a higher stability and softening point and also lower deformation is expected to be an alternative to overcome the weaknesses of asphalt concrete mixtures. Also cheaper operational costs are the selling point of asbuton that needs to be watch out for. The aim of this study was to determine the Optimum Asphalt Content or also known as KAO of the mixing between asbuton and asphalt in order to obtain a mixture composition that meet the AC-BC characteristics requirements. The research method used in this paper is the experimental method and analyzed in accordance with the General Specification of Bina Marga 2018 revision 2. Based on the results of research conducted in the laboratory of University of Muhammadiyah Parepare, the asphalt mixture with Asbuton LGA type 50/30 with a content of 7%, 8% and 9% KAO was obtained at 6.75%. From the three variations, AC-BC with the addition of 7% LGA has the best stability with a MQ value of 319.93 kg/mm
References
Bolung, A. L., Sendow, T. K., & Waani, J. E. (2019). Perbandingan Kriteria Marshall Pada Campuran Aspal Panas (Hrs-Wc) Yang Menggunakan Asbuton Modifikasi (Retona Blend 55) Dengan Aspal Penetrasi 60/70. Jurnal Sipil Statik, 7(11), 1537-1546
Hasdianti, W. N., Macmoed, B. R., & Lahay, I. H. (2023). Analisa Kadar Air Dan Kadar Bitumen Aspal Buton Pada Pt. Karya Megah Buton Mengunakan Metode Sokhlet. Jambura Industrial Review, 3(1), 1-10
Kementerian Pekerjaan Umum dan Perumahan Rakyat. (2020). Spesifikasi Umum Bina Marga 2018 untuk Pekerjaan Konstruksi Jalan dan Jembatan (Revisi 2). Jakarta: Direktorat Jenderal Bina Marga
Maizuar, M. (2023). Karakteristik Marshall Campuran Ac-Bc Menggunakan Ethylene Vinyl Acetate Sebagai Asphalt Modifier. Jurnal Teknologi Terapan and Sains, 4(1), 891-902
Misbah. (2015). Pengaruh Variasi Kadar Aspal Terhadap Nilai Karakteristik Campuran Panas Aspal Agregat (AC-BC) Dengan Pengujian Marshall. Jurnal Teknik Sipil Institut Teknologi Padang, 2(1), 41–48
Muhammad, M., Purwandito, M., & Basrin, D. (2022). Rencana Campuran Aspal Ac-Bc (Aspal Concreate-Binder Course) Dengan Menggunakan Abu Batu Kapur Sebagai Tambahan Filler. Jurnal Engineering Development, 2(1), 8-15
Muslimin, E. (2022). Studi Pengaruh Kehilangan Fraksi Agregat Halus Pada Spesifikasi Ream Terhadap Campuran Aspal Porus. Gorontalo Journal of Infrastructure & Science Engineering, 5(2), 53-58
Nawir, D., & Zultan, A. (2020). Analisis Kinerja Campuran Aspal Beton (AC-BC) Menggunakan Liquid Asbuton Dengan Penambahan Serpih Sampah HDPE (High Density Polyethylene). Borneo Engineering : Jurnal Teknik Sipil, 4(1), 78-90
Pinangkaan, V., Sompie, T. P. F., & Sudarno, S. (2022). Analisis Perbandingan Karakteristik antara AC-WC Asbuton dengan Cold Paving Hot Mix Asbuton (CPHMA). Semesta Teknika, 25(1), 60-70
Rahmat, A., & Fadly, I. (2022). Analisis Material Agregat Pada Campuran Asphalt Concrete-Binder Course (Studi Kasus: Agregat Sungai Saddang Kabupaten Enrekang). Jurnal Karajata Engineering, 2(2), 61-69
Sriharyani, L., & Tholib, A. (2019). Perubahan Parameter Marshall Akibat Perbedaan Jumlah Tumbukan pada Asphalt Concrete- Binder Coarse (AC-BC) Gradasi Kasar. TAPAK (Teknologi Aplikasi Konstruksi): Jurnal Program Studi Teknik Sipil, 8(1), 53-65
Subagyo, G. W. (2020). Kinerja Modulus Resilien Campuran Beraspal Panas Asphalt Concrete Binder Course (AC-BC) Yang Mengandung Recycled Concrete Aggregate. Widyakala Journal, 7(1), 1-6
Sumiati, S., Mahmuda, M., & Puryanto, P. (2019). Keunggulan Asbuton Pracampuran Dan Aspal Shell Pada Campuran Aspal Beton (AC-BC). Jurnal Poli-Teknologi, 18(1), 53-64
Winarno, B., Budi, K. C., Sumargono, S., Candra, A. I., Muslimin, S., & Sudjati, S. (2020). Pengaruh Abu Batu Sebagai Filler Terhadap Kinerja Aspal Beton AC-WC Pada Test Marshall. Civilla: Jurnal Teknik Sipil Universitas Islam Lamongan, 5(2), 468-475
Yendri, O., & Septiandi, W. (2023). Kajian Kemampuan Campuran Aspal-Beton (AC-BC) Dengan Asbuton Cair Yang Diisi Dengan Serpihan HDPE (High Density Polyethylene). Jurnal Teknik Gradien, 15(1), 9-19
Yuniarti, S., Rahman, R., & Alpius. (2020). Studi Karakteristik Campuran AC-BC Berdasarkan Limbah Kantong Plastik Sebagai Bahan Tambah. PCEJ, 2(2), 70–76
Yunus, I., & Annisa, H. (2023). Analisis Penggunaan Asbuton Butir B50/30 Terhadap Kinerja Campuran Ac-Wc Dengan Variasi Temperatur Pemadatan. Jurnal Teknik Sipil Universitas Lamappapoleonro, 2(1), 38-45
.png)
.png)